关键词： AZ31 Mg alloy   B-ECAP   microstructure   texture evolution   mechanical properties  

摘要： In this work,a novel type of short-process deformation technology of Mg alloys,bifurcation-equal channel angular pressing(B-ECAP),was proposed to refine grain and improve the basal *** cylindrical billets were first compressed into the die cavity,then sequentially flowed downward through a 90°corner and two 120°shear *** total strain of B-ECAP process could reach 3.924 in a single *** results of microstructure observation showed that DRX occurred at upsetting process in the die cavity and completed at position *** grains were refined to 6.3μm at being extruded at 300℃ and grew obviously with the extrusion temperature *** shear tress induced by 900 corner and two 120°shear steps resulted in the basal poles of most grains tilted to extrusion direction(ED)by±25°.Compared with the original billets,the extruded sheets exhibited higher yield strengths(YS),which was mainly attributed to the grain *** higher Schmid factor caused by ED-tilt texture resulted in a fracture elongation(FE)more than that of the original bar in ED,while was equivalent to that in transverse direction(TD).As the extrusion temperature increased,the variation of UTS and YS in ED and TD decreased gradually without ductility obviously decrease.

关键词： 伤口愈合   生物相容性   绷带   电击伤   敷料贴   电场   电极   一次性  

摘要： 电绷带是带电的绷带吗?它怎么用?它会不会导致使用者被电击伤?它是一种利用电场促进慢性伤口愈合的绷带:主体是一次性水动力敷料,一侧有电极,另一侧有一个小型生物相容性电池。使用时,伤者先将敷料贴在伤口上,使电极与伤口接触;然后将水滴到电池上,激活它。此后,电绷带会持续数小时产生电场,加快伤口愈合的速度,而不会伤害人体。

关键词： 车身轻量化   自冲铆接   镁合金   铝合金   力学性能  

摘要： 镁合金材料在车身轻量化制造方面具有巨大的潜力和应用空间,选取不同厚度的AZ31B镁合金和5083铝合金薄板材料进行自冲铆接,并通过拉伸实验和扫描电镜分析接头的静力学性能及微观组织。结果表明:自冲铆接能实现对AZ31B镁合金和5083铝合金薄板的有效连接;板厚搭配均匀的自冲铆接接头的整体力学性能最优;镁板厚度较小的自冲铆接接头的失效形式均为上板断裂,其余两组自冲铆接接头的失效形式均为下板拉脱;3组不同镁板厚度组合的自冲铆接接头断口均呈脆性断裂形貌。

关键词： 硫酸钙   难愈合创面   治疗   进展  

摘要： 慢性难愈合创面是指因各种开放性骨折、大面积撕脱伤、Ⅱ度以上烧伤、糖尿病足、压力性损伤、下肢静脉性溃疡等引起,经一个月以上规范治疗后仍未愈合也无明显愈合倾向的创面[1]。反复换药、静脉使用抗生素、封闭负压引流等方法常不能控制感染源,达到治愈的目的。彻底清创和控制创面感染是治疗的关键,但是过度的清创会加大骨质及软组织等的缺失,可能造成患者部分功能丧失或形态毁损,全身应用抗生素在局部难以达到有效的杀菌浓度,易产生耐药性及肝肾不良反应。

关键词： AZ31B镁合金   板材   纵波-平辊轧制   微观取向  

摘要： 为探究纵波轧制(longitudinal wave rolling,LR)对AZ31B镁合金微观取向的影响,对AZ31B镁合金板材400℃/20 min和450℃/20 min热处理后,利用振幅0.35 mm,周期4 mm的纵波波纹轧辊和平轧辊进行了波-平和平-平二道次轧制。借助EBSD分析了轧制后板材波谷、波腰及波峰处的晶粒度及取向。结果表明:板材热处理后,基面织构强度和平均晶粒尺寸均降低,其中450℃/20 min热处理后基面织构强度下降显著,但其平均晶粒尺寸增加;400℃/20 min+LR后板材的平均晶粒尺寸显著降低,波峰和波谷处的基面织构强度较热处理试样增强,波腰基面织构强度几乎不变,然而因波峰和波谷大量晶粒分别沿RD的相反方向发生了偏转,故整体宏观织构强度显著降低;二道次轧制后,400℃/20 min+纵波-平辊轧制(longitudinal wave rolling+flat rolling,LFR)后波峰和波谷处的基面织构强度较400℃/20 min+LR后对应位置显著降低,而波腰强度显著增强,同时各处平均晶粒尺寸进一步降低。400℃/20 min+平辊-平辊轧制(flat rolling+flat rolling,FFR)后相比400℃/20 min+LFR,其基面织构强度弱于波腰而强于波峰和波谷处。故400℃下LFR后板材与FFR后板材的整体基面织构强度接近。450℃/20 min+FFR后板材相比400℃/20 min+FFR后板材,其基面织构强度显著降低,{0001}<1120>类型织构占比更低,同时平均晶粒尺寸增大。

关键词： VW53镁合金   孪生行为   室温压缩   力学性能  

摘要： 研究了Mg-5.65Gd-3.15Y-0.48Zr(VW53)镁合金室温压缩过程中的孪生行为及其对组织性能的影响,通过将固溶态VW53镁合金在室温下进行不同应变的压缩试验,然后利用OM、SEM和EBSD等技术对试样进行微观组织观察和分析,并测试试样的维氏显微硬度。结果表明:VW53镁合金在室温压缩过程中,主要产生{1012}拉伸孪晶和{1121}拉伸孪晶,随着应变增加{1012}孪晶会形核、生长、合并、甚至吞并整个晶粒,而{1121}孪晶不会发生显著的扩展合并。孪晶界可以阻碍位错移动和分割细化晶粒,随着应变的增加,孪晶界相互交截和分割细化晶粒的程度提高,可以有效提高VW53镁合金力学性能。

关键词： 肋骨骨折   可降解   内固定   聚合物   镁合金  

摘要： 肋骨骨折是最常见的胸部外伤性疾病,对于部分严重的患者,需要通过外科手术植入内固定材料以重建肋骨的稳定性。临床所使用的肋骨内固定材料大多不可吸收,部分患者会因为术后体内异物滞留而产生胸部不适感或心理焦虑,需要二次手术将其取出,从而显著增加患者的痛苦及就医成本。可降解的肋骨内固定材料由于植入后会被机体逐步降解吸收,能有效解决上述问题。然而,目前临床获批使用的可降解材料适应证较窄,二次手术的问题仍未得到全面解决。经表面涂层处理的镁合金材料在诸多可降解材料中显示出巨大的优势,有望成为肋骨骨折的首选内固定材料。

关键词： 镁合金板带   X射线测厚仪   在线测厚  

摘要： X射线测厚仪主要应用在镁合金板带连续可逆轧制过程中,可以连续精准测量实时厚度。介绍了X射线测厚仪的基本工作原理,以及在实际生产过程中的应用,极大提升了板带厚度控制的准确性,提高了生产效率、产品合格率和产品质量。

关键词： 格栅   镁合金   低压铸造   浇注系统设计   数值模拟  

摘要： 以ZM6格栅铸件为对象,利用浇注系统设计的水力学原理,采用垂直缝隙式浇道对格栅铸件低压铸造浇注系统进行了优化设计,通过ProCAST软件对浇注过程中流动场和温度场分布规律进行了模拟和分析。结果显示,采用水力学原理,增加缝隙浇道与铸件接触的面积及立筒数量,可显著提高充型效果,降低铸件凝固过程各处的温度梯度;采用优化后的浇注系统设计实现了格栅铸件的成形,配合专用磨头进行后期铸件修整,能够满足格栅铸件批量生产的要求。

关键词： 镁合金   镁空气电池   微观组织   电化学性能   放电性能  

摘要： 采用电化学技术和镁空气电池放电测试系统地研究了Mg-x Sr(x=0.2%,0.5%,1%,2%和4%)(质量分数)5种合金作为镁空气电池阳极材料的耐蚀性及放电性能。结果表明,在镁合金中添加适量的Sr元素时,可以有效的增强合金的耐蚀性和电化学活性。在所研究的阳极里,Mg-2Sr阳极在所有电流密度下都具有最高且相对稳定的放电电压且表现出最好的放电性能,在40 mA/cm 2下具有最高的阳极效率,为68%。随着Sr含量的进一步增加,过量的第二相加速了自腐蚀,合金的耐蚀性和放电性能下降。